Cold rolled ribbed bars
The current position:Home >> Products >> Cold rolled ribbed bars >> Browse
Cold rolled ribbed bars
Author: Source: Views:1751次 Updated:2014-11-15 14:59:32

Cold rolled ribbed steel bar is made of hot rolled wire rod by multichannel cold-rolled, reducing a rib rolling and after stress relief form of a steel bar with two or three surface crescent. Cold rolled ribbed steel bar is the upgrading production of cold drawn low carbon steel wire in prestressed concrete members. In cast-in-situ concrete structure, steel can be instead ofⅠgrade steel bar, in order to save steel, is better one in the same kind of cold rolled steel。

Cold-rolled ribbed steel grades by the CRB and reinforced the tensile strength of the minimum. C、R 、B, respectively (cold - rolled), cold-rolled ribbed (ribbed), steel bar (bars) three words of the first letter in English.CRB550, CRB650, cold rolled ribbed bar CRB800, CRB970 and CRB1170 five grades.CRB550 for ordinary reinforced concrete with steel.

Cold rolled ribbed bar has the following advantages.
1. high strength steel, It can save material and reduce the project cost.CRB550 compared with hot rolled round steel bar, used for cast-in-place structure (especially the floor roof) can save 35%-40% steel. Such as considering no hook, steel more savings. According to the steel market price, using a ton of cold rolled ribbed steel bar, can cut down the cost of steel 800 RMB.
2. cold-rolled ribbed steel bar the bond anchorage between reinforcement and concrete performance is good. Used in components, therefore, fundamentally eliminate the anchorage zone of cracking, steel wire slip and failure phenomenon, and improves the end bearing capacity and crack resistance of the component; In reinforced concrete structure, the crack width is better than round bar, even smaller than hot rolling thread steel.
3. Elongation than the same kind of cold steel cold rolled ribbed bar.

3.1 Steel Bar Grade and Chemical Composition

Wire Rod Size and Chemical Composition for Cold Rolled Ribbed Steel Bar

 Steel Bar Grade

 Wire rod Grade

Chemical Composition (quality score)/% 

 C

 Si

Mn 

 V、Ti

 S

CRB550 

 Q215

 0.09~0.15 

  ≤0.30

 0.25~0.55 

  -

 ≤0.050

≤0.045 

 Q215

 0.14~0.22

  ≤0.30

 0.25~0.55 

  -

 ≤0.050

 ≤0.045

 

2. Dynam Capability and Technic Capability for cold rolled ribbed steel bar

 Grade

 Rpo.2/Mpa
  ≥

 Rm/Mpa≥

 Tensility /%≥

 Bend Test 180。

 Bend Times

 The stress relaxation
initial value should be equivalent to 70% of the engineering tensile strength

 A 11.3

A100 

 1000h Relaxation /%≥

 CRB550

 500

550 

 8

 ―

D=3d 

 ―

 ―

 

Note: 1. In the table D for bending diameter, d for reinforced nominal diameter.
         2. Steel bar by cold working status of delivery. Allow low temperature tempering treatment after cold rolling.

         3.When to bend test, the bending parts surface shall not crack. Bending radius of repeated bending test: reinforced nominal diameter 4 mm, 5 mm, 6 mm, the bending radius 10 mm, 15 mm, 15 mm.

        4. The strength of the reinforced than Rm/Rpo. 2 ratios should be 1.03 or higher. The supply and demand both sides agreement use Agt≥2.0% available instead of A.

         5. The supplier on the basis of guarantee 1000 h relaxation rate of qualified, allowed to use the method of determine 1000 h relaxation.

         6. CRB550 reinforced nominal diameter in the range of 4 ~ 12 mm. CRB550 and above brand of nominal diameter 4 mm, 5 mm, 6 mm.

2. Dynam Capability and Technic Capability for cold rolled ribbed steel bar

 

【Home】  【Return】

Home  |  About us  |  Products  |  Engineering case  |  Company honor  |  Dynamic news  |  Technical data  |  Contact us 

   friendly links:WIRE MESH CACHINE | STEEL CONSTRUCTION | DUST REMOVAL EQUIPMENT

Address:Anping County Industrial Park East    Technical support:.

Tel:0318-7800071  Fax:0318-7800072    Ji ICP 16023864    

煤矿用支护网,河南带肋钢筋网片,大直径钢筋焊网,钢筋焊接网,山东钢筋网片,桥梁钢筋网片,钢笆片,大型钢筋网片生产厂家,河北泰德钢筋加工有限公司